Polyester T100 ki baze sou Distribisyon an poliyiretàn Prepolymer

HJ-3170

HJ-3175

HJ-3180

HJ-3185

NCO pousan kontni

2.3±0.2

2.7±0.2

3.0±0.2

3.5±0.2

Dansite25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Viskozite80 degree /mpa·s

2200-2500

1800-2100

1700-2000

1500-1800

Aparans nan 25degre

Blan solid

MixTemperaturedegre

Prepolymer/Moca

85 degre / 115 degre

85 degre / 115 degre

85 degre / 115 degre

85 degre / 115 degre

Tan jèl/min

35-45

20-30

15-18

12-16

Tan vulkanizasyon (h)

25-16

25-16

25-16

25-16

Pwopriyete Fizik

Dite (Shore A)

70±2

75±2

80±2

85±2

Fòs rupture (Mpa)

30-35

35-40

38-43

43-47

100 pousan Modil (Mpa)

8-10

8-10

8-10

9-10

300 pousan modil (Mpa)

16-17

16-17

16-18

16-18

Elongasyon nan kraze (pousan)

600-650

620-680

650-700

650-720

Fòs chire (KN/m)

55-65

60-75

85-90

90-100

Konpresyon pèmanan deformation pousan

4-6

4-6

4-6

2-4

DIN pèt abrasion（mm³）

Mwens pase oswa egal a 50

Mwens pase oswa egal a 50

Mwens pase oswa egal a 45

Mwens pase oswa egal a 45

Rezilyans pousan /25degre

25-28

23-26

22-24

18-22

Aplikasyon pwodwi: Woulo, kawotchou min, ekran klasifikasyon, pawa tiyo, kouple, senti CONVEYOR min, grate enprime, endistriyèl kaster, netwayaj tiyo, pawa ponp, roue selil flotasyon ak lòt pwodwi.

Detay operasyon:

Apre degazing vakyòm nan 80-85 degre, prepolymer la melanje ak MOCA fonn pou Distribisyon ak vulkanizasyon. Li apwopriye pou operasyon manyèl ak mekanik.

Depo:

Sere nan yon kote ki fre ak sèk epi itilize pi vit ke posib apre ouvèti; Si li pa ka itilize nan yon sèl fwa, li dwe sele ak nitwojèn; Dezyèm ouvèti a bezwen itilize pou defoaming, ak peryòd depo orijinal la se sis mwa.

anbalaj:

20kg oswa 200kgron tanbou

HJ-3135

HJ-3190

HJ-3190A

HJ-3190C

NCO pousan kontni

3.5±0.2

4.3±0.2

4.3±0.2

4.2±0.2

Dansite25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Viskozite80 degree /mpa·s

1500-1800

1100-1400

1200-1500

1200-1500

Aparans nan 25degre

Blan solid

MixTemperaturedegre

Prepolymer/Moca

85 degre / 115 degre

80 degre / 115 degre

80 degre / 115 degre

80 degre / 115 degre

Tan jèl/min

16-22

8-12

6-9

12-16

Tan vulkanizasyon (h)

25-16

25-16

25-16

25-16

Pwopriyete Fizik

Dite (Shore A)

85±2

90±2

90±2

90±2

Fòs rupture (Mpa)

43-47

45-52

43-50

46-53

100 pousan Modil (Mpa)

8-10

8-10

8-10

8-10

300 pousan modil (Mpa)

14-16

15-17

14-16

16-18

Elongasyon nan kraze (pousan)

600-750

580-700

600-710

550-650

Fòs chire (KN/m)

95-110

100-120

95-110

110-125

Konpresyon pèmanan deformation pousan

4-6

2-4

2-4

2-4

DIN pèt abrasion（mm³）

Mwens pase oswa egal a 50

Mwens pase oswa egal a 40

Mwens pase oswa egal a 48

Mwens pase oswa egal a 40

Rezilyans pousan /25degre

20-23

16-19

18-22

15-18

Aplikasyon pwodwi: Woulo, kawotchou min, ekran klasifikasyon, pawa tiyo, kouple, senti CONVEYOR min, grate enprime, endistriyèl kaster, netwayaj tiyo, pawa ponp, roue selil flotasyon ak lòt pwodwi.

Detay operasyon:

Apre degazing vakyòm nan 80-85 degre, prepolymer la melanje ak MOCA fonn pou Distribisyon ak vulkanizasyon. Li apwopriye pou operasyon manyèl ak mekanik.

Depo:

Sere nan yon kote ki fre ak sèk epi itilize pi vit ke posib apre ouvèti; Si li pa ka itilize nan yon sèl fwa, li dwe sele ak nitwojèn; Dezyèm ouvèti a bezwen itilize pou defoaming, ak peryòd depo orijinal la se sis mwa.

anbalaj:

20kg oswa 200kgron tanbou

HJ-3193

HJ-3195

HJ-3195A

HJ-3197

NCO pousan kontni

4.7±0.2

5.0±0.2

5.5±0.2

6.5±0.2

Dansite25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Viskozite80 degree /mpa·s

1000-1300

900-1200

900-1300

800-1100

Aparans nan 25degre

Blan solid

MixTemperaturedegre

Prepolymer/Moca

80 degre / 115 degre

75 degre / 115 degre

75 degre / 115 degre

75 degre / 115 degre

Tan jèl/min

6-9

7-10

5-8

3-6

Tan vulkanizasyon (h)

25-16

25-16

25-16

25-16

Pwopriyete Fizik

Dite (Shore A)

93±2

95±2

95±2

97±2

Fòs rupture (Mpa)

48-55

50-55

48-53

46-55

100 pousan Modil (Mpa)

8-10

9-10

9-10

9-10

300 pousan modil (Mpa)

16-18

18-22

16-18

18-22

Elongasyon nan kraze (pousan)

450-600

400-550

530-700

400-550

Fòs chire (KN/m)

100-120

110-130

110-130

115-130

Konpresyon pèmanan deformation pousan

2-4

2-4

2-4

2-4

DIN pèt abrasion（mm³）

Mwens pase oswa egal a 45

Mwens pase oswa egal a 45

Mwens pase oswa egal a 45

Mwens pase oswa egal a 45

Rezilyans pousan /25degre

15-18

14-16

13-16

12-15

Aplikasyon pwodwi: Woulo, kawotchou min, ekran klasifikasyon, pawa tiyo, kouple, senti CONVEYOR min, grate enprime, endistriyèl kaster, netwayaj tiyo, pawa ponp, roue selil flotasyon ak lòt pwodwi.

Detay operasyon:

Apre degazing vakyòm nan 80-85 degre, prepolymer la melanje ak MOCA fonn pou Distribisyon ak vulkanizasyon. Li apwopriye pou operasyon manyèl ak mekanik.

Depo:

Sere nan yon kote ki fre ak sèk epi itilize pi vit ke posib apre ouvèti; Si li pa ka itilize nan yon sèl fwa, li dwe sele ak nitwojèn; Dezyèm ouvèti a bezwen itilize pou defoaming, ak peryòd depo orijinal la se sis mwa.

anbalaj:

20kg oswa 200kgron tanbou